* GN-1 MACROMOLECULE ADHESIVE FILM
|
|||||||||||||
|
* GN-1 MACROMOLECULE ADHESIVE FILM
|
|||||||||||||
Product Name
* GN-1 MACROMOLECULE ADHESIVE FILM
Raw material
Resin from DuPont US
Market share
40% of Chinese market and expanding market in India, U.A.E.,
Russia, Mexico, Vietnam and others.
Function
Used for producing all kinds of aluminum composite panel
(GB/T17748-1999) and other types of metal-plastic composite panels
One Popular Bonding Method
1.Hot pressing method: heating at both sides
2.Bonding working temperature: 200°C~210°C
3.Bonding pressure: 4kg/cm2
4.Bonding pressing time: above 30~60 seconds
5.Metal surface condition: phosphorus or chrome metalized and
degreasing handling in advance, keep it clean from dust, moisture,
impurity and etc.
6.Heater: electroheat tube or heating pressing roller
* GN – 1 HT
Main Characteristics
1.Possessing powerful and stable adhesive property
2.Possessing easiness for process and application
3.Resisting boiling water
4.Resisting temperature difference under diverse environments
Main parameters
Peremater / item | Unit | Test standard | Value |
Fusion point | ℃ | DSC.D3418 | 126 |
Peak Possessing Temp. | ℃ | - | ≥200 |
Density | g/cm3 | ASTMD 790 | 0.920 |
Tensile strength (at break) | Kg/cm 2 | ASTMD 638 | 110-130 |
Elongation (at break) | % | ASTMD 638 | ≥350 |
Rigidity | D-scale | ASTMD 2240 | 45 |
VIAT Softening temperature | ℃ | ASTMD 1525 | 100 |
180 ° peeling strength | N/mm | GB/T2790 | ≥10 |
Width | M | - | 1.00~2.00 |
Thickness specification | mm | GB7125-86 | 0.035~0.05~0.08 |
Length | M | - | 980-1400 |
Remark: The data is classical and would be realized or surpassed if, and only if, the ACP production are under proper working situation with needed temperature, pressure, speed and others.
Package Mode: Damp-proof carton. Special orders are also welcome.
* GN – 1 LT
Main parameters
Peremater / item | Unit | Test standard | Value |
Fusion point | ℃ | DSC.D3418 | 105 |
Peak Possessing Temp. | ℃ | - | ≥150 |
Density | g/cm3 | ASTMD 790 | 0.938 |
Tensile strength (at break) | Kg/cm 2 | ASTMD 638 | 100-120 |
Elongation (at break) | % | ASTMD 638 | ≥300/350 |
Rigidity | D-scale | ASTMD 2240 | 45 |
VIAT Softening temperature | ℃ | ASTMD 1525 | 65 |
180 ° peeling strength | N/mm | GB/T2790 | ≥7 |
Width | M | - | 1.00~2.00 |
Thickness specification | mm | GB7125-86 | 0.035~0.05~0.08 |
Length | M | - | 980-1400 |
Remark: The data is classical and would be realized or surpassed if, and only if, the ACP production are under proper working situation with needed temperature, pressure, speed and others.
See more products from this supplier.
Do you want to show products of your own company? Join FREE now!